TY - JOUR
T1 - Spectral Tuning, Stabilities under External Exposures, and Spontaneous Enhancement of Emission Intensity in Grown-into-Glass All-Inorganic Metal Halide Perovskite Nanocrystals
AU - Kang, Fengwen
AU - Du, Yongping
AU - Yang, Ze
AU - Boutinaud, Philippe
AU - Wubs, Martijn
AU - Xu, Jie
AU - Ou, Haiyan
AU - Li, Dongzhe
AU - Zheng, Kaibo
AU - Tarekegne, Abebe T.
AU - Sun, Guohuan
AU - Xu, Xuhui
AU - Xiao, Sanshui
PY - 2023/1
Y1 - 2023/1
N2 - Herein, the grown-into-glass (GIG) CsPbBr3:Ln3+ (Ln = La, Lu) nanocrystals (NCs) are designed and fabricated using an in situ nanocrystallization method. It is shown that a substitution of Pb2+ sites with Ln3+ ions leads to a blueshift of emission position induced by an increase of the bandgap of CsPbBr3. Additionally, the GIG-samples are found to feature excellent photoluminescent (PL) properties after being immersed respectively in water for 300 days at room temperature, boiling water for 12 h, and corrosive environments for 24 h, as well as recoverable PL intensity either after several cycles of heat-cooling experiments or after being continuously exposed to a 405 nm laser irradiation. Besides, a spontaneous enhancement of 20-25% of emission intensity during the 1-2.5 hours' stage of a 405 nm laser irradiation, attributed to the radiative recombination of charge carriers that can be de-trapped from trapping levels upon the laser light irradiation and that then spontaneously reinforces the emission intensity, is observed in the GIG-CsPbBr3:Ln3+ NCs. Finally, a white light-emitting prototype, with a CIE chromaticity coordinate at (0.4110, 0.3706), a color rendering index of 89 and a correlated color temperature of 3363 K is realized by combining the GIG-CsPbBr3 NCs, YAG:Ce and CaWO4:Eu phosphors.
AB - Herein, the grown-into-glass (GIG) CsPbBr3:Ln3+ (Ln = La, Lu) nanocrystals (NCs) are designed and fabricated using an in situ nanocrystallization method. It is shown that a substitution of Pb2+ sites with Ln3+ ions leads to a blueshift of emission position induced by an increase of the bandgap of CsPbBr3. Additionally, the GIG-samples are found to feature excellent photoluminescent (PL) properties after being immersed respectively in water for 300 days at room temperature, boiling water for 12 h, and corrosive environments for 24 h, as well as recoverable PL intensity either after several cycles of heat-cooling experiments or after being continuously exposed to a 405 nm laser irradiation. Besides, a spontaneous enhancement of 20-25% of emission intensity during the 1-2.5 hours' stage of a 405 nm laser irradiation, attributed to the radiative recombination of charge carriers that can be de-trapped from trapping levels upon the laser light irradiation and that then spontaneously reinforces the emission intensity, is observed in the GIG-CsPbBr3:Ln3+ NCs. Finally, a white light-emitting prototype, with a CIE chromaticity coordinate at (0.4110, 0.3706), a color rendering index of 89 and a correlated color temperature of 3363 K is realized by combining the GIG-CsPbBr3 NCs, YAG:Ce and CaWO4:Eu phosphors.
KW - CsPbBr
KW - glass
KW - laser lighting
KW - luminescence sustainability and enhancement
KW - spectral tuning
U2 - 10.1002/lpor.202200166
DO - 10.1002/lpor.202200166
M3 - Article
AN - SCOPUS:85139995312
SN - 1863-8880
VL - 17
JO - Laser and Photonics Reviews
JF - Laser and Photonics Reviews
IS - 1
M1 - 2200166
ER -