Electron microscopy of some molybdenum oxide phases after use as catalysts in oxidative ammonolysis and ammoxidation of toluene

Research output: Contribution to journalArticle

Bibtex

@article{90dc622f435b48a8b1063008ba1b7a25,
title = "Electron microscopy of some molybdenum oxide phases after use as catalysts in oxidative ammonolysis and ammoxidation of toluene",
abstract = "Five molybdenum oxide samples, subjected to conditions of oxidative ammonolysis and ammoxidation of toluene at 450 and 460°C, respectively, have been characterized using X-ray diffraction, scanning and transmission electron microscopy, and specific surface area measurements. In oxidative ammonolysis, the relatively large, freshly prepared MoO3 crystals are reduced to smaller MoO2 crystals with a crystallite size of 5–30 nm. This process gives a perfectly pseudomorphous product with pores less than 5 nm. The specific surface area increases from <0.1 m2/g to almost 40 m2/g. In subsequent ammoxidation, MoO2 transforms first into orthorhombic Mo4O11 and finally into MoO3. The crystals of Mo4O11 are about 1 μm in diameter, and their formation leads to a decrease of specific surface area. The original MoO3 morphology is retained even after the sequence of transformation as follows: MoO3 → MoO2 → Mo4O11 (→MoO3). In some cases, the new generation of MoO3 crystals grows parallel to the original MoO3 crystals.",
author = "Staffan Hansen and Arne Andersson",
year = "1988",
doi = "10.1016/0022-4596(88)90162-4",
language = "English",
volume = "75",
pages = "225--243",
journal = "Journal of Solid State Chemistry",
issn = "0022-4596",
publisher = "Elsevier",
number = "2",

}