Atomistic investigation of functionalized polyethylene-alumina interfacial strength and tensile behaviour

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

We study the adhesion and tensile behaviour of bi-layer interfaces comprising polyethylene, doped with carbonyl and hydroxyl functional groups emanating from ozone treatment, and - by means of density functional theory and classical atomistic modelling. The results show that the deformations are localized within the polymer and comprise chain slip, disentanglement and detachment from the substrate, where only the latter is notably affected by the doping. The binding energies and excess forces associated with the detachment of functional groups from the alumina substrate are of the order of 1.7 eV and 1 nN, respectively, for both types. Although such forces do not affect the maximum peak stress notably, they give rise to spikes in the traction-separation curves following the fibril formation and promote increased total work of fracture.

Detaljer

Författare
Enheter & grupper
Externa organisationer
  • Tetra Pak AB
  • Malmö University
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Teknisk mekanik
Originalspråkengelska
Artikelnummer110075
Antal sidor10
TidskriftComputational Materials Science
Volym187
StatusPublished - 2021 feb 1
PublikationskategoriForskning
Peer review utfördJa

Nedladdningar

Ingen tillgänglig data