Diffusion of a mixture of cations and anions dissolved in water

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

In service life modeling of concrete, the ion transport in the pore solution is crucial. The main deterioration phenomena associated
with ions in the pore solution are (1) corrosion due to external chloride ions reaching the embedded reinforcement bars; (2) carbonation
due to presence of dissolved carbon dioxide (which will form carbonic acid with water) supplied from the surrounding air; and (3) leaching
of hydroxide ions from the pore solution to the surrounding environment. Models dealing with diffusion of ions are usually based on
the mass balance equations for the individual diffusing ions together with constitutive relations for the mass density flows and for the mass
exchange among the constituents. The important consequences of electroneutrality among the diffusing ions, however, is often omitted in
models dealing with diffusion of ions in the pore solution of concrete. Here a method will be examined that allows diffusion of different
ions in water, which satisfies both the electroneutrality requirement and the mass balance laws. For simplicity the effect of built-up electric
double layers on the charged pore walls will not be treated.

Detaljer

Författare
  • Björn Johannesson
Enheter & grupper
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Materialteknik

Nyckelord

Originalspråkengelska
Sidor (från-till)1261-1270
TidskriftCement and Concrete Research
Volym29
Utgåva nummer8
StatusPublished - 1999
PublikationskategoriForskning
Peer review utfördJa

Relaterad forskningsoutput

Björn Johannesson, 2000, Division of Building Materials, LTH, Lund University. 502 s.

Forskningsoutput: AvhandlingDoktorsavhandling (sammanläggning)

Visa alla (1)