Functionalizing polystyrene with N-alicyclic piperidine-based cations via Friedel-Crafts alkylation for highly alkali-stable anion-exchange membranes

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift


title = "Functionalizing polystyrene with N-alicyclic piperidine-based cations via Friedel-Crafts alkylation for highly alkali-stable anion-exchange membranes",
abstract = "Different anion-exchange membranes (AEMs) based on polystyrene (PS) carrying benzyltrimethyl ammonium cations are currently developed for use in alkaline fuel cells and water electrolyzers. However, the stability of these state-of-the-art cations needs to be further improved. Here, we introduce highly alkali-stable mono- and spirocyclic piperidine-based cations onto PS by first performing a superacid mediated Friedel-Crafts alkylation using 2-(piperidine-4-yl)propane-2-ol. This is followed by quaternization of the piperidine rings either using iodomethane to produce N,N-dimethylpiperidinium cations or cyclo-quaternizations using 1,5-dibromopentane and 1,4-dibromobutane, respectively, to obtain N-spirocyclic quaternary ammonium cations. Thus, it is possible to functionalize up to 27{\%} of the styrene units with piperidine rings, and subsequently achieve complete quaternization. The synthetic approach ensures that all the sensitive β-hydrogens of the cations are present in ring structures to provide high stability. AEMs based on these polymers show high alkaline stability and less than 5{\%} ionic loss was observed by 1H NMR spectroscopy after 30 days in 2 M aq. NaOH at 90 °C. AEMs functionalized with N,N-dimethylpiperidinium cations show a higher stability than the ones carrying N-spirocyclic quaternary ammonium. Careful analysis of the latter revealed that the rings formed in the cyclo-quaternization are more prone to degrade via Hofmann elimination than the rings introduced in the Friedel-Crafts reaction. AEMs with an ion exchange capacity of 1.5 meq g-1 reach a hydroxide conductivity of 106 mS cm-1 at 80 °C under fully hydrated conditions. The AEMs are further tuned and improved by blending with polybenzimidazole (PBI). For example, an AEM containing 2 wt{\%} PBI shows reduced water uptake and much improved robustness during handling, and reaches 71 mS cm-1 at 80 °C. The study demonstrates that the critical alkaline stability of PS-containing AEMs can be significantly enhanced by replacing the benchmark benzyltrimethyl ammonium cations with N-alicyclic piperidine-based cations.",
author = "Joel Olsson and Pham, {Thanh Huong} and Patric Jannasch",
note = "Publication Date: June 1, 2020",
year = "2020",
doi = "10.1021/acs.macromol.0c00201",
language = "English",
volume = "53",
pages = "4722--4732",
journal = "Macromolecules",
issn = "0024-9297",
publisher = "The American Chemical Society (ACS)",
number = "12",