High resolution strain mapping of a single axially heterostructured nanowire using scanning X-ray diffraction

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

Axially heterostructured nanowires are a promising platform for next generation electronic and optoelectronic devices. Reports based on theoretical modeling have predicted more complex strain distributions and increased critical layer thicknesses than in thin films, due to lateral strain relaxation at the surface, but the understanding of the growth and strain distributions in these complex structures is hampered by the lack of high-resolution characterization techniques. Here, we demonstrate strain mapping of an axially segmented GaInP-InP 190 nm diameter nanowire heterostructure using scanning X-ray diffraction. We systematically investigate the strain distribution and lattice tilt in three different segment lengths from 45 to 170 nm, obtaining strain maps with about 10−4 relative strain sensitivity. The experiments were performed using the 90 nm diameter nanofocus at the NanoMAX beamline, taking advantage of the high coherent flux from the first diffraction limited storage ring MAX IV. The experimental results are in good agreement with a full simulation of the experiment based on a three-dimensional (3D) finite element model. The largest segments show a complex profile, where the lateral strain relaxation at the surface leads to a dome-shaped strain distribution from the mismatched interfaces, and a change from tensile to compressive strain within a single segment. The lattice tilt maps show a cross-shaped profile with excellent qualitative and quantitative agreement with the simulations. In contrast, the shortest measured InP segment is almost fully adapted to the surrounding GaInP segments. [Figure not available: see fulltext.].

Detaljer

Författare
Enheter & grupper
Externa organisationer
  • Northwestern University
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Den kondenserade materiens fysik

Nyckelord

Originalspråkengelska
TidskriftNano Research
StatusE-pub ahead of print - 2020 jun 21
PublikationskategoriForskning
Peer review utfördJa