Highly conductive hydroxide exchange membranes containing fluorene-units tethered with dual pairs of quaternary piperidinium cations

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

In the pursuit of anion exchange membranes (AEMs) with high alkaline stability and hydroxide conductivity, we have prepared and characterized a series of poly(fluorene alkylene)s in which each fluorene unit was functionalized with dual pairs of quaternary piperidinium cations on flexible alkyl spacer chains. First, ether-free precursor polymers were synthesized in superacid mediated polyhydroxyalkylations of 2,2,2-trifluoroacetophenone, 9,9-dimethyl-2,7-diphenyl-9H-fluorene, and different amounts of 2,7-dibromo-9,9-bis(6-bromohexyl)-fluorene to regulate the degree of bromoalkylation. Subsequently, the bromoalkyl side chains were utilized to introduce bis-piperidinium (bisPip) cations via Menshutkin reactions. These materials formed transparent and mechanically strong AEMs upon casting. At 80 °C, the hydroxide conductivity of bisPip AEMs reached 85 and 150 mS cm–1 at ion-exchange capacities (IECs) of 2.0 and 2.8 mequiv g–1, respectively. Moreover, the bisPip AEMs showed high alkaline stability with an ionic loss of merely 6% following immersion in 5 M aq. NaOH solution for a period of 168 h at IEC = 2.8 mequiv g–1. Under these conditions, 1H NMR data indicated that a β-hydrogen in an alkyl spacer chain was about 8 times more susceptible to attacks by hydroxide ions than a β-hydrogen in a piperidinium ring. In comparison, corresponding AEMs with fluorene units functionalized with monoPip cations (i.e., a single pair of piperidinium cations per fluorine unit) showed lower conductivity and alkaline stability under the same conditions, demonstrating the advantage of locally concentrating the cations in the polymer structure by employing
bisPip side chains.

Detaljer

Författare
Enheter & grupper
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Polymerteknologi
  • Polymerkemi
  • Materialkemi
  • Fysikalisk kemi

Nyckelord

Originalspråkengelska
Artikelnummer119376
Antal sidor40
TidskriftJournal of Membrane Science
Volym632
Tidigt onlinedatum2021
StatusPublished - 2021 aug 15
PublikationskategoriForskning
Peer review utfördJa