Paperboard Mechanical Properties at Fracture

Forskningsoutput: Kapitel i bok/rapport/Conference proceedingKonferenspaper i proceeding

Abstract

Paperboard mechanical properties at fracture during uniaxial tests is an interplay between available elastic energy at fracture and the fracture energy needed to separate the sample into two parts. A test at a critical length, the load vs. elongation curve immediately falls from a point of instability to zero load. Whereas, a test at a stable length give a stable descending load-elongation curve with no discontinuous drop of the load.

Tests, less than the stable length, give the cohesive law of the paper. The cohesive law is fully characterized by the tensile strength, the maximum slope of the curve and a parameter represents the shape of the law. From the parameters two length measure are defined giving a ratio 푔. It is shown that the ratio 2푔 is the ratio the between the critical length and the stable length.

The finding is applied to an infinite paper sheet with a crack length of 2푎 loaded with a remote loading. It is shown that length of the processes zone is proportional to the critical length of the paperboard and independent of an applied load, at small scale yielding (using the Dugdale model).

Detaljer

Författare
Enheter & grupper
Externa organisationer
  • Tetra Pak AB
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Pappers-, massa- och fiberteknik
Originalspråkengelska
Titel på värdpublikationProceedings of the International Paper Physics Conference 2019
FörlagTAPPI
Sidor57-68
Antal sidor12
ISBN (tryckt)978-151089394-8
StatusPublished - 2019
PublikationskategoriForskning
Peer review utfördJa
Evenemang2019 International Paper Physics Conference - Indianapolis, USA
Varaktighet: 2019 maj 52019 maj 8

Konferens

Konferens2019 International Paper Physics Conference
LandUSA
Ort Indianapolis
Period2019/05/052019/05/08