Performance of ZrO2-supported Nb- and W-oxide in the gas-phase dehydration of glycerol to acrolein

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

Gas-phase dehydration of glycerol to acrolein is studied over tungsten and niobium oxide supported on monoclinic zirconia. Supported tungsten oxide is slightly better than supported niobia with initial yields to acrolein around 78% and 75%, respectively, at complete conversion of glycerol. No synergy is observed using mixed structures with W and Nb. The addition of oxygen to the feed has almost no effect on the yield to acrolein but reduces the deactivation rate. XPS and HRTEM imaging reveals that deactivation is due to formation of an amorphous layer on the surface, consisting of adsorbed high-boiling compounds and coke. Regeneration experiments show that the catalysts are effectively regenerated in flowing air. Characterization of the catalysts with Raman, FTIR, and pyridine adsorption reveals that the active surface structure is polymeric oxide exposing W=O and/or Nb=O species and Bronsted acidic W OH and/or Nb OH groups. The results show that Bronsted acidic sites are required for the catalyst to be active and selective to acrolein. (c) 2012 Elsevier Inc. All rights reserved.

Detaljer

Författare
Enheter & grupper
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Kemiteknik
  • Kemi

Nyckelord

Originalspråkengelska
Sidor (från-till)93-109
TidskriftJournal of Catalysis
Volym297
StatusPublished - 2013
PublikationskategoriForskning
Peer review utfördJa