Radial tunnel diodes based on InP/InGaAs core-shell nanowires

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

We report on the fabrication and characterization of radial tunnel diodes based on InP(n+)/InGaAs(p+) core-shell nanowires, where the effect of Zn-dopant precursor flow on the electrical properties of the devices is evaluated. Selective and local etching of the InGaAs shell is employed to access the nanowire core in the contact process. Devices with an n+-p doping profile show normal diode rectification, whereas n+-p+ junctions exhibit typical tunnel diode characteristics with peak-to-valley current ratios up to 14 at room temperature and 100 at 4.2 K. A maximum peak current density of 28 A/cm2 and a reverse current density of 7.3 kA/cm2 at VSD = −0.5 V are extracted at room temperature after normalization with the effective junction area.

Detaljer

Författare
Enheter & grupper
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Den kondenserade materiens fysik
  • Nanoteknik
Originalspråkengelska
Artikelnummer113501
TidskriftApplied Physics Letters
Volym110
Utgivningsnummer11
StatusPublished - 2017 mar 13
PublikationskategoriForskning
Peer review utfördJa