Vertically Aligned CsPbBr3 Nanowire Arrays with Template-Induced Crystal Phase Transition and Stability

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskrift

Abstract

Metal halide perovskites show great promise for a wide range of optoelectronic applications but are plagued by instability when exposed to air and light. This work presents low-temperature solution growth of vertically aligned CsPbBr3 nanowire arrays in AAO (anodized aluminum oxide) templates with excellent stability, with samples exposed to air for 4 months still exhibiting comparable photoluminescence and UV stability to fresh samples. The single-crystal nanowire length is adjusted from ∼100 nm to 5 μm by adjusting the precursor solution amount and concentration, and we observe length-to-diameter ratios as high as 100. Structural characterization results indicate that large-diameter CsPbBr3 nanowires have an orthorhombic structure, while the 10 nm- and 20 nm-diameter nanowires adopt a cubic structure. Photoluminescence shows a gradual blue-shift in emission with decreasing nanowire diameter and marginal changes under varying illumination power intensity. The CsPbBr3-nanowires/AAO composite exhibits excellent resistance to X-ray radiation and long-term air storage, which makes it promising for future optoelectronic applications such as X-ray scintillators. These results show how physical confinement in AAO can be used to realize CsPbBr3 nanowire arrays and control their morphology and crystal structure.

Detaljer

Författare
Enheter & grupper
Forskningsområden

Ämnesklassifikation (UKÄ) – OBLIGATORISK

  • Nanoteknik
Originalspråkengelska
Sidor (från-till)4860-4868
Antal sidor9
TidskriftJournal of Physical Chemistry C
Volym125
Utgåva nummer8
StatusPublished - 2021 feb 11
PublikationskategoriForskning
Peer review utfördJa