Branched-gallium phosphide nanowires seeded by palladium nanoparticles

Palladium nanoparticles were produced by a chemical reagent-free and versatile method called spark ablation with control over particle size and density. These nanoparticles were used as catalytic seed particles for gallium phosphide nanowire growth by metalorganic vapour-phase epitaxy. Controlled growth of GaP nanowires using significantly small Pd nanoparticles between 10 and 40 nm diameter was achieved by varying several growth parameters. Low V/III ratios below 2.0 promote higher Ga incorporation into the Pd nanoparticles. Moderate growth temperatures under 600 °C avoid kinking and undesirable GaP surface growth. In addition, a second batch of palladium nanoparticles of concentration up to 1000 particles μm⁻² was deposited onto the GaP nanowires. Subsequently, three-dimensional nanostructures evolved, with branches growing along the surface of the GaP nanowires. The GaP nanowires revealed a zinc blende structure with multiple twinning and a PdGa phase at the tip of the nanowires and branches.