Fully aromatic block copolymers for fuel cell membranes with densely sulfonated nanophase domains

Shogo Takamuku, Patric Jannasch

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskriftPeer review

Sammanfattning

Two multiblock copoly(arylene ether sulfone)s with similar block lengths and ion exchange capacities (IECs) were prepared by a coupling reaction between a non-sulfonated precursor block and a highly sulfonated precursor block containing either fully disulfonated diarylsulfone or fully tetrasulfonated tetraaryldisulfone segments. The latter two precursor blocks were sulfonated via lithiation-sulfination reactions whereby the sulfonic acid groups were exclusively placed in ortho positions to the many sulfone bridges, giving these blocks IECs of 4.1 and 4.6 meq·g−1, respectively. Copolymer membranes with IECs of 1.4 meq·g−1 displayed well-connected hydrophilic nanophase domains and had decomposition temperatures at, or above, 300 °C under air. The copolymer with the tetrasulfonated tetraaryldisulfone segments showed a proton conductivity of 0.13 S·cm−1 at 80 °C under fully humidified conditions, and surpassed that of a perfluorosulfonic acid membrane (NRE212) by a factor of 5 at –20 °C over time.
Originalspråkengelska
Sidor (från-till)474-480
TidskriftMacromolecular Rapid Communications
Volym32
Nummer5
DOI
StatusPublished - 2011

Bibliografisk information

First published online on 29 Dec. 2010



The information about affiliations in this record was updated in December 2015.
The record was previously connected to the following departments: Polymer and Materials Chemistry (LTH) (011001041)

Ämnesklassifikation (UKÄ)

  • Kemi

Fingeravtryck

Utforska forskningsämnen för ”Fully aromatic block copolymers for fuel cell membranes with densely sulfonated nanophase domains”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här