Long term evolution of microstructure and stress around tin whiskers investigated using scanning Laue microdiffraction

Johan Hektor, Jean Sébastien Micha, Stephen A. Hall, Srinivasan Iyengar, Matti Ristinmaa

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskriftPeer review

Sammanfattning

Scanning Laue microdiffraction was used to study the evolution of the microstructure and the stress field around two tin whiskers during ageing for up to 21 months. In the heterogeneous stress fields obtained, localised ridges of high compressive stress leading to the root of the whiskers were found. Due to the evolution of the intermetallic compound in the interface between the copper substrate and the tin coating, the stress field was also evolving with time. The temporal evolution of the stress field indicates that the regions supplying material to the whisker root is changing with time, highlighting that whisker growth is a highly dynamical process. During the experimental campaign, a new surface feature appeared in a grain boundary within the scanned area of the sample. The new feature had a twinning relationship with one of the neighbouring grains, a similar twin relation was also seen for one of the two larger whiskers. It is suggested that tin atoms diffuse out from the ridges of high compressive stress to the nearby, less compressed grain boundaries along which diffusion towards the root of the whisker occurs. The observations made from the Laue diffraction measurements also suggest that whiskers form in regions where the gradient in hydrostatic stress is large and that they grow to relax compressive stresses.

Originalspråkengelska
Sidor (från-till)210-221
Antal sidor12
TidskriftActa Materialia
Volym168
DOI
StatusPublished - 2019

Ämnesklassifikation (UKÄ)

  • Metallurgi och metalliska material

Fingeravtryck

Utforska forskningsämnen för ”Long term evolution of microstructure and stress around tin whiskers investigated using scanning Laue microdiffraction”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här