Post-nucleation evolution of the liquid-solid interface in nanowire growth

Carina B. Maliakkal, Daniel Jacobsson, Marcus Tornberg, Kimberly A. Dick

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskriftPeer review

Sammanfattning

We study using in situ transmission electron microscopy the birth of GaAs nanowires from liquid Au-Ga catalysts on amorphous substrates. Lattice-resolved observations of the starting stages of growth are reported here for the first time. It reveals how the initial nanostructure evolves into a nanowire growing in a zincblende 111 or the equivalent wurtzite0001 direction. This growth direction(s) is what is typically observed in most III-V and II-VI nanowires. However, the reason for this preferential nanowire growth along this direction is still a dilemma. Based on the videos recorded shortly after the nucleation of nanowires, we argue that the lower catalyst droplet-nanowire interface energy of the {111} facet when zincblende (or the equivalent {0001} facet in wurtzite) is the reason for this direction selectivity in nanowires.

Originalspråkengelska
Artikelnummer105607
TidskriftNanotechnology
Volym33
Nummer10
DOI
StatusPublished - 2022 mars 5

Bibliografisk information

Publisher Copyright:
© 2021 The Author(s). Published by IOP Publishing Ltd.

Ämnesklassifikation (UKÄ)

  • Den kondenserade materiens fysik

Fingeravtryck

Utforska forskningsämnen för ”Post-nucleation evolution of the liquid-solid interface in nanowire growth”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här