Segregation dynamics of a Pd-Ag surface during CO oxidation investigated by NAP-XPS

Marie D. Strømsheim, Ingeborg Helene Svenum, Mehdi Mahmoodinia, Virgínia Boix, Jan Knudsen, Hilde J. Venvik

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskriftPeer review

1 Citering (SciVal)

Sammanfattning

The dynamic changes in composition in the near-surface region of a Pd75%Ag25%(100) single crystal were monitored using near-ambient pressure x-ray photoelectron spectroscopy (NAP-XPS) during CO oxidation under oxygen rich conditions at a total pressure of 1.1 mbar. Six CO oxidation temperature cycles were investigated at different heating rates and maximum temperatures of 450 °C or 600 °C. It was found that the history of the bimetallic sample plays an important role, as the CO2 formation profile varies depending on initial conditions, and previous heating rates and maximum temperatures. In terms of CO coverage effects, normal, reversed and no hysteresis behaviour were all observed. In agreement with previous modelling predictions, the NAP-XPS data confirm a dynamic segregation behaviour upon heating/cooling where the amount of Pd in the surface region decreases with increasing temperature. Nevertheless, the Pd 3d5/2 core level relative area assessment is not fully capable of capturing all the surface dynamics inferred from the temperature dependent CO2 formation profiles, due to the probing depth. While residing at ambient temperature in the reaction mixture, however, there is a build-up of adsorbed CO at the surface showing that CO induces segregation of Pd to the topmost surface layer under these conditions. In total, this suggests that the segregation is kinetically relatively facile during temperature cycling, and that adsorbate coverage is the main controlling factor for the surface termination.

Originalspråkengelska
Sidor (från-till)265-273
TidskriftCatalysis Today
Volym384-386
Utgåva0
Tidigt onlinedatum2021
DOI
StatusPublished - 2022

Ämnesklassifikation (UKÄ)

  • Kemiska processer
  • Biokemi och molekylärbiologi
  • Den kondenserade materiens fysik

Fingeravtryck

Utforska forskningsämnen för ”Segregation dynamics of a Pd-Ag surface during CO oxidation investigated by NAP-XPS”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här