Synthesis and melt-spinning of partly bio-based thermoplastic poly(cycloacetal-urethane)s toward sustainable textiles

Forskningsoutput: TidskriftsbidragArtikel i vetenskaplig tidskriftPeer review

2 Citeringar (SciVal)

Sammanfattning

A rigid diol with a cyclic acetal structure was synthesized by facile acetalation of fructose-based 5-hydroxymethyl furfural (HMF) and partly bio-based di-trimethylolpropane (di-TMP). This diol (Monomer T) was copolymerized with potentially biobased flexible polytetrahydrofuran and diisocyanates to prepare thermoplastic poly(cycloacetal-urethane)s. A modified one step solution polymerization protocol resulted in relatively high molecular weights (Mn ~ 41.5 -98.9 kDa). All the obtained poly(cycloacetal-urethane)s were amorphous with tuneable glass transition temperatures up to 104 °C. Thermogravimetric analysis indicated that these polymers were thermally stable up to 253 °C and had a relatively high pyrolysis char residue, which may indicate potential inherent flame resistance. Melt rheology measurements were performed to determine a suitable processing window between 165-186 °C, after which the polymer was successfully melt-spun into ~150 meters of homogeneous fibres at 185 °C. The resulting fibres could be readily hydrolysed under acidic conditions, resulting in partial
recovery of the original chemical building blocks.
Originalspråkengelska
Sidor (från-till)4942-4953
TidskriftPolymer Chemistry
Volym12
Utgåva34
DOI
StatusPublished - 2021

Bibliografisk information

First published 10 Aug 2021

Ämnesklassifikation (UKÄ)

  • Polymerteknologi
  • Textil-, gummi- och polymermaterial
  • Polymerkemi
  • Materialkemi

Fingeravtryck

Utforska forskningsämnen för ”Synthesis and melt-spinning of partly bio-based thermoplastic poly(cycloacetal-urethane)s toward sustainable textiles”. Tillsammans bildar de ett unikt fingeravtryck.

Citera det här